6mm heat soaked tempered toughened glass

6mm Heat Soak Glass is also called 6mm HST glass. The aim of 6mm heat soak tempered glass is to reduce the risk of spontaneous.

What is the heat soak test?

Heat soak testing is a destructive test.

Tempered Glass is put into a heat Soak Oven and brought to and held at a temperature of 555 degrees Fahrenheit for two hours.

The most glass containing Nickel Sulphide will shatter during this process and thus be eliminated from the glass.

Heat soaking is a process utilized to expose NiS inclusions in the tempered glass before the glass reaches the field.

It involves placing tempered glass inside a chamber and raising the temperature to approximately 290°C to accelerate nickel sulfide expansion.

This is intended to cause glass containing nickel sulfide inclusions to break in the heat soak chamber, thus reducing the risk of potential breakage in the field.

Features:

1. Heat soak glass carries the risk of reducing the compressive stress in tempered glass.

2. Heat soak test reduces the risk of breakage due to inclusions

3. Heat Soak Testing protects against spontaneous breakage of toughened glass.

4. The Heat Soak Testing process adds longevity to toughened glass by eliminating foreign bodies that occur in raw materials of float glass especially “Nickel Sulphide (NiS)”.

EdgeWork: Flat/Pencil/beveled, Matt/Polished Edge

Corners Work: Safety Corners, Cutting Corners, Radius Corners

Drilling holes and Cutouts

Application:

As heat soak glass reduce the risk of glass self blew and use widely for place needs high attention of safety consideration, mostly use the areas
need safety considerations, such as:

1. Glass facade, glass curtain wall

2. Glass fence, glass balustrade, glass railings

3. Glass partition, glass wall, glass partition wall

4. Glass door, glass shower door, glass shower screen